WebCrazing can often be eliminated simply by applying a thinner glaze coat. With some glazes, a thinner coat is not an option, but often a slight decrease in glaze thickness will stop crazing. 2. Add increasing amounts … WebCrazing: internal fracturing without a change of the surface texture. It might be seen when light transmits through transparent or translucent material and it can also exist in opaque …
Defining the Difference Between a „Crack“ and a „Craze“
WebAug 16, 2014 · Temperature will cause the lens coating to expand and contract. If the hard coat on the lens is uneven (as is often the case with back-side spin coating), it will expand unevenly. The uneven expansion under the AR stresses the AR coating, and causes it to crack/craze. This is why 'high end' AR coatings use a dip coat. Crazing is the phenomenon that produces a network of fine cracks on the surface of a material, for example in a glaze layer. Crazing frequently precedes fracture in some glassy thermoplastic polymers. As it only takes place under tensile stress, the plane of the crazing corresponds to the stress direction. The effect … See more Crazing occurs in polymers, because the material is held together by a combination of weaker Van der Waals forces and stronger covalent bonds. Sufficient local stress overcomes the Van der Waals force, allowing a … See more Crazing is also used as a term in odontology to describe fine cracks in the enamel of teeth. See more • Understanding Crazing • Crazing Concrete Surfaces Archived 2006-05-17 at the Wayback Machine See more Crazing is also seen on single ply roofing membranes, joint sealant, and on concrete when good concrete practices are not followed. See more Crazing is a glaze defect of glazed pottery. Characterised as a spider web pattern of cracks penetrating the glaze, it is caused by See more The root sense of the word crazy in English, meaning “to shatter, crush, or break,” dates to the 1300s. The metaphorical senses familiar today derive from crazing in pottery: crazy meaning “diseased or sickly” dates to about 1570; “of unsound mind” … See more svgs in react
Crazing and Cracking in Anodizing Products Finishing
Webapply the glaze less thickly. add more flux to the glaze to make it more fluid. decrease the content of zinc or rutile in the glaze. where zinc is used, try calcining half or all of the zinc content. increase the maturing temperature of the glaze. hold the kiln at the glaze maturing temperature for a soaking period of up to two hours. WebJul 27, 2024 · Crazing is a network of fine cracks usually in the shape of a hexagonal pattern of varying size from 5 to 75 mm. This defect occurs in plastered wall surface because over troweling of rich mix or sand containing excessive amount of dust. Crazing crack is a surface crack that is due to shrinkage and weathering action. Web4.2.1 Crazes. Crazing is an underlying mode of polymer fracture and has been widely studied.8–10,13–16,18,21,27,28 Crazing develops when excessive tensile stress is … skeleton with flamethrower